International Journal of Nano Dimension (Int. J. Nano Dimens.) Nano composite PEBAX®/PEG membranes: Effect of MWNT filler on CO2/CH4 separation Volume 5 (2014) Issue 3, July 2014 2024 02 29 Nano composite PEBAX®/PEG membranes: Effect of MWNT filler on CO2/CH4 separation 10.7508/ijnd.2014.03.006 EN S. Habibzare Department of Chemical Engineering, North Tehran Branch, Islamic Azad University, Tehran, Iran. M. Asghari Energy Research Institute, University of Kashan, Ghotb-e-Ravandi Ave., Kashan, Iran. A. Djirsarai Energy Research Institute, University of Kashan, Ghotb-e-Ravandi Ave., Kashan, Iran. Journal Article 2024 02 29 The performances of two-phase polymer-liquid PEBAX®/polyethylene glycol (PEG) and three-phase polymer-liquid-solid PEBAX®/PEG/MWNT thin film composite membranes for CO2 and CH4 permeation were studied. The effect of temperature and MWNT/PEBAX® ratio on single gas (CO2 and CH4) permeability was investigated. The permeation of both gases was measured at different temperatures from 303 to 323 ˚K. The results exhibited that the PEBAX®/PEG/MWNT membrane had better permeability for CO2 in comparison to the PEBAX®/PEG membrane, whereas CO2/CH4 selectivities in both membranes were almost the same; i.e. MWNT filler promoted the performance of PEBAX®/PEG membrane in CO2/CH4 Separation. Also, the permeability increases with temperature in all experiments. For the three-phase PEBAX®/PEG/MWNT membrane, CO2 permeability was determined 221 Barrer in 323˚K and the selectivity was obtained as 23 in 303 ˚K.